Physical Properties | Test Method | Nominal Value | Unit | |
Density | ISO1183 | 0.921 | g/cm3 | |
Melt Mass-Flow Rate (MFR) | ISO 1183 | 1.9 | g/10min | |
Hardness | ||||
Shore Hardness(shore D) | ISO868 | 45 | ||
Mechanical Properties | ||||
Tensile Modulus | ISO572-2 | 175 | Mpa | |
Tensile Strength | Yield | ISO527-2 | 9.0 | MPa |
Break | 13.0 | |||
Tensile Strain(Break) | ISO527-2 | 850 | % | |
Modulus of Elasticity | Internal Method | 250 | Mpa | |
Thermal | ||||
Vicat Softening Temperature(DSC) | ISO306/A50 | 89.0 | Centidegree | |
Melting Temperature(DSC) | DIN 53765 | 108 | Centidegree | |
Peak Crystallization Temperature(DSC) | DIN 53765 | 97.0 | Centidegree | |
Heat of Fusion | DIN 53765 | 110 | J/g | |
Electrical | ||||
Volume Resistivity | ASTM D257 | 8.5E+15 | Ohm.cm | |
Dielectric Strength | ASTM D149 | 30.0 | KV/mm | |
Dielectric Constant(60HZ) | ASTM D150 | 2.2 | % | |
Dissipation Factor(60HZ) | ASTM D150 | 0.00050 |
HDPE cable material Property | Typical Value | |
Mass density g/cm 3 | 0.941-0.959 | |
Melt flow Rate(190 centidegree /2.16kg)g/10min | ≤1.0 | |
Tensile yield strength MPa | ≥19.0 | |
Flexural modulus Mpa | ≥965 | |
Elongation@ break % | ≥400 | |
Impact Embrittlement temperature centidegree | MAX -118 | |
Dielectric Constant | 100KHZ | 2.32 |
1MHZ | 2.31 | |
Loss Tangent | 100KHZ | MAX 0.0001 |
1MHZ | MAX 0.0001 | |
Volume resistivity OHM-CM | MIN 1x10 15 |
Item | Test condition | Test Method | Value | Unit |
Density | | ISO 1183 | 0.944-0.955 | g/cm3 |
MFR | 190°C/2.16kg | ISO 1133 | 0.03-0.07 | g/10min |
Tensile strength at yield | | ISO 527-2 | 22 | MPa |
Elongation at break | | ISO 527-2 | >350 | % |
ESCR | F50,50°C,100% | ASTM D-1693A | 1000 | h |
VICAT | | ASTM D-1525 | 126 | °C |
Item | Test Condition | Test Method | Value | Unit |
Density | | ISO 1183 | 0.950~0.955 | g/cm |
MFR | 190°C/2.16kg | ISO 1133 | 1.7~2.5 | g/10min |
Tensile strength at yield | | ISO 527-2 | 24 | MPa |
Elongation at break | | ISO 527-2 | >600 | % |
Item | Test Condition | Test Method | Value | Unit |
MFR | 190°C/2.16kg | ASTM D-1238 | 20 | g/10min |
Density | --- | ASTM D-792 | 0.954 | g/cm3 |
Tensile strength at yiled | --- | ASTM D-638 | 28 | MPa |
Elongation at break | --- | ASTM D-638 | 250 | % |
Impact tensile strength | --- | ASTM D-1822 | 42 | kJ/m2 |
ESCR | | ASTM D-1693 | 3 | --- |
VACIT | --- | ASTM D-1525 | 127 | °C |
Product Categories : Plastic Resin